Name

FT-C910 fluorine Teflon oil paint top coating

FT-C fluorotetrafluorocarbon oil topcoat is a high-efficiency, multi-purpose, chemically cured fluorocarbon copolymer as a raw material, a two-component room temperature curing coating, which has excellent durability, protection, decoration and anticorrosion. Excellent performance.

官网

A detailed description

product manual	Surface treatment
FT-C fluorotetrafluorocarbon oil topcoat is a high-efficiency, multi-purpose, chemically cured fluorocarbon copolymer as a raw material, a two-component room temperature curing coating, which has excellent durability, protection, decoration and anticorrosion. Excellent performance. The long-term outdoor use and artificial accelerated aging tests show that the fluorocarbon bonds on the molecular chain of fluororesins can resist the degradation of ultraviolet rays and heat and salt, and show extremely excellent durability, making the fluorocarbon coatings as perfect as new for a long time, and Reduce maintenance requirements.	All surfaces must be intact, dry, and clean, free of grease, dirt, mold release agents, solidified materials, wind-resistant materials, welding slag, loose paint films, and other foreign materials. New surface: In order to make the paint performance better, the surface of the steel should be sandblasted to meet the Sa2.5 standard. There should be no sand or dust on the surface. Paint immediately after sandblasting to prevent the surface from rusting or contaminating again. Old paint surface: The old paint film must be completely removed, and then surface treated with reference to the new surface, at least sandblasted to SSPC-SP10 or SSI-Sa21 / 2. For best appearance and protection, the primer or middle coat must be intact and level.
use	Specification data
It is suitable for covering decorative protection of metal, wood, decorative sheet, construction, etc. It can also be used for covering coating of epoxy, polyurethane, acrylic and other coatings. Can comprehensively improve its protection, decoration and service life.	Gloss: Low light or high light Color: customer color (including solid color, metallic color, pearl color, etc.) Volume solids content: about 48% Theoretical coverage rate: about 16 m² / liter (based on 25 micron dry film) Specific gravity: 1.30 kg / liter (different colors vary) Dry with fingers: 4 hours @ 20 ℃ Fully cured: 7 days @ 20 ℃
Features
Super weather resistance and durability Excellent corrosion and chemical resistance Has excellent anti-fouling ability, the paint surface can be brushed with ordinary cleaners The paint film is dense and hard, impact resistance and abrasion resistance

Construction parameters：

Mixing ratio: base material (FT-CxXXX): curing agent (F298-C910) = 16: 1 (weight ratio)

Thinner: FT-9

Construction method: Airless spraying, general spray brushing

Dilution ratio (about paint consumption): 5% 15% 5%

Activation period: 6 hours @ 20 ℃

Nozzle size: 0.017 "-0.019"

Spray pressure: 150 kg / cm2 (Airless spraying information is for reference only, and can be adjusted when practical)

Tool cleaning: FT-9

Film thickness: wet film: 100 microns dry film: 40 microns (see note)

Recoating interval: minimum: 10 hours @ 20 ℃, maximum: 30 days @ 20 ℃

Construction instructions

The application temperature range is 5 ℃ -40 ℃. In addition, the surface temperature of the steel should be higher than 3 ° C above the dew point to prevent condensation.

Ventilation, paint film thickness, humidity, dilution ratio and other factors will affect the drying speed.

Film thickness: The film thickness can be modified according to the design requirements or different areas, but this will change the normal range of the coating rate, drying time and recoating interval is 40-80 microns.

Physical parameters of temperature change (40-60 microns dry film)
Construction surface temperature（℃）	5	10	20	30	40
Touch dry / about	8h	4h	2h	1h	0.5h
Time for condensation, humidity and light rain after construction	7day	3day	24h	16h	8h
Fully cured（R.H70%)	30day	21day	7day	3day	2day
Self-recoating interval	6day	2day	1day	8h	2h
maximum	Unlimited	Unlimited	Unlimited	Unlimited	Unlimited

Note: It is strictly forbidden to contact with water during the construction process, and construction is not recommended when the humidity exceeds 85%. The curing agent should be kept dry during storage. In hot weather construction, the activation period will be significantly shortened. Once the paint has thickened, it should be reconstituted.

Precautions

Ensuring good ventilation in all enclosed areas is of great significance to the safety and performance of the constructors. It is recommended to ventilate the storage tank in two steps. First, pump fresh and dry air into all parts of the storage tank, especially in areas where air cannot flow. Second, use the explosion-proof exhaust fan to extract the solvent vapor in the lowest area of the tank. During the entire application and drying process of the paint, fresh air must be continuously pumped to extract the solvent vapor in the lowest area of the tank to ensure that the solvent completely evaporates from the paint film. The paint film of the storage tank must be cured under ventilation for 7 days (20 ° C). The lower the temperature, the longer the curing time.

Packaging and storage

Goods type: paint

Packaging specifications: Different packaging specifications are available.

Storage: Store in a cool, dry place, and do not expose to the sun.

Limitation of Liability

The technical data described in this article is accurate to the best of our knowledge at the time of publication, but is subject to change without notice. We guarantee that our products comply with the descriptions in this article, but do not make any other commitments or warranties, express or implied, including saleable or applicable to special purposes. If there is any liability, it is limited to replacing the product or refunding the purchase price, and will not be responsible for labor, labor costs or other losses caused by it.